NYLON 66/6
PHYSICAL PROPERTIES
| Density |
0.039-0.0419 lb/in3 |
| Water Absorption |
0-10 % |
| Moisture Absorption at Equilibrium |
2.1-4 % |
| Water Absorption at Saturation |
0-12 % |
| Moisture Vapor Transmission |
356 cc-mil/100 in²-24hr-atm |
| Oxygen Transmission |
88.9 cc-mil/100 in²-24hr-atm |
| Environmental Stress Crack Resistance |
1000 hour |
| Linear Mold Shrinkage |
0.008-0.011 in/in |
| Linear Mold Shrinkage, Transverse |
0.01-0.011 in/in |
| Melt Flow |
60 g/10 min |
MECHANICAL PROPERTIES
| Hardness, Rockwell R |
76-118 |
| Tensile Strength, Ultimate |
4790-11600 psi |
| Tensile Strength, Yield |
2180-12300 psi |
| Elongation @ break |
5-640 % |
| Elongation @ Yield |
5-50 % |
| Tensile Modulus |
46.4-537 ksi |
| Flexural Modulus |
27.6-508 ksi |
| Flexural Yield Strength |
1310-15200 psi |
| Compressive Yield Strength |
2470 psi |
| Taber Abrasion, mg/1000 Cycles |
10 |
| Shear Strength |
8560 psi |
| Izod Impact, Notched |
0.562- NB |
| Izod Impact, Notched Low Temp |
0.918-3.5 ft-lb/in |
| Charpy Impact, Unnotched |
28.6-NB |
| Charpy Impact, Notched Low Temp |
1.9 ft-lb/in2 |
| Charpy Impact |
1.43-16.7 ft-lb/in2 |
| Coefficient of Friction, Static |
0.5-1 |
| Tensile Creep Modulus, 1 hour |
145000 psi |
| Tensile Creep Modulus, 1000 hours |
129000 psi |
ELECTRICAL PROPERTIES
| Electrical Resistivity |
1E+11-1E+15 ohm-cm |
| Dielectric Constant |
3.2-6 |
| Dielectric Constant, Low Frequency |
3.7-4.1 |
| Dielectric Strength |
457-3050 kV/in |
| Dissipation Factor |
0.02-0.3 |
| Dissipatin Factor, Low Frequency |
0.01--0.03 |
| Surface Resistance |
1E+10-1E+15 ohm |
| Comparative Tracking Index |
600 V |
THERMAL PROPERTIES
| CTE, linear 200 C |
36.1-47.2 µ in/in-°F |
| CTE, linear 20° C Transvers to Flow |
50 µ in/in-°F |
| Melting Point |
374-500°F |
| Maximum Service Temperature, Air |
135-311°F |
| Deflection Temperature at 0.46 MPa |
180-435°F |
| Deflection Temperature at 1.8 MPa |
135-194°F |
| Vicat Softening Point |
482°F |
| Flammability, UL94 |
V-0 |
| Oxygen Index |
34-37% |
OPTICAL PROPERTIES
| Haze |
1-4 % |
| Gloss |
130-145% |
| Transmission, Visible |
80% |
PROCESSING PROPERTIES
| Processing Temperature |
482-536°F |
| Rear Barrel Temperature |
482°F |
| Middle Barrel Temperatue |
482°F |
| Front Barrel Temperature |
500°F |
| Mold Temperature |
122°F |
| Drying Temperature |
176°F |
this is text meant just to take up lots of space at the bottom of the page, so that if
there is only a table or something in the content part of this page, the content still
takes up the majority of the screen. if there is not any text here, then sometimes there
will be just a table here, and the left navigation bar to the left will be kinda wide...
|
|